EN 10277:2018 standard
W.NR.: 1.1180
Non-alloy special steel
heat analysis according to the EN ISO 683-1:2018 standard
| C % | Si % | Mn % | P % | S % | Cr % | Ni % | Mo % | Cu % | Cr+Mo+Ni % | |
| From | 0,32 | 0,10 | 0,50 | – | 0,020 | – | – | – | – | – |
| To | 0,39 | 0,40 | 0,80 | 0,025 | 0,040 | 0,40 | 0,40 | 0,10 | 0,30 | 0,63 |
according to the EN 10277:2018 standard
| Thickness mm |
Rolled + peeled rolled ( +SH ) |
Cold drawn ( +C ) |
|||
| hardness HB | Rm (MPa) | Rp0,2 minimum | Rm (MPa) | A5 % | |
| (MPa) | minimum | ||||
| ≥5≤10 | 510 | da 650 a 1000 | 6 | ||
| >10≤16 | 420 | da 600 a 950 | 7 | ||
| >16≤40 | da 156 a 204 | da 520 a 700 | 320 | da 580 a 880 | 8 |
| >40≤63 | da 156 a 204 | da 520 a 700 | 300 | da 550 a 840 | 9 |
| >63≤100 | da 156 a 204 | da 520 a 700 | 270 | da 520 a 800 | 9 |
* Delivery condition: as rolled.
Weldability:
It can be welded quite well without any precautions.
Hardenability:
Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned, it hardens only till a certain depth, inversely proportional to diameter, like all non-alloy steels with medium-high carbon content.
Notes:
CORRESPONDENCE WITH OTHER STANDARDS (purely as an indication):
| UNI 7845 | DIN 17200 | AISI-SAE | AFNOR 35-552 |
| C35 | Cm35 | 1035 | XC38H1u |